Nickel 200 And 201 Plate

Gnee Steel (Tianjin) Co., Ltd. is one of the most professional manufacturers and suppliers of nickel 200 and 201 plate in China. With abundant experience, we warmly welcome you to wholesale customized nickel 200 and 201 plate from our factory. For price consultation, contact us.

Nickel 200 and 201 plate offer outstanding corrosion resistance to caustic soda and other alkalis. They perform best in reducing environments but can also be used under oxidizing conditions when a passive oxide film is formed. They are used in aerospace, chemical and petrochemical processing, food processing, and marine and water treatment applications. Nickel 200 and 201 are both highly ductile across a wide temperature range and can be easily welded and processed by standard shop fabrication practices.

Nickel 200 and 201 plate can be easily welded and processed by standard shop fabrication practices.

Hot Forming

Hot bending operations should be performed in the temperature range of 1600º to 2250ºF (870º to 1230ºC). In any operation, care should be taken to avoid heating Nickel 200 and 201 plate above the upper temperature limit of 2250ºF (1230ºC).

Cold Forming

Nickel 200 and 201 can be worked by any conventional cold-forming method. The forming characteristics are comparable to those of mild steel; however, because of the higher elastic limits of Nickel 200 and 201, greater power will be needed to perform the operations. Severe forming can be done manually but will require intermediate anneals to restore the alloy’s softness.

Machining

Nickel 200 and 201 plate should be machined in the annealed condition whenever possible. These grades have the propensity to work harden, making it necessary to utilize low cutting speeds and requiring the cutting tool to stay engaged at all times. An adequate chip depth is important in order to avoid contact with the previously formed work-hardened zone. Liquid cold forming lubricants should be utilized to assure optimal heat dissipation.

Welding

Nickel 200 and 201 plate can be joined by a variety of welding procedures including inert gas and resistance welding. Welding practices are similar to those used to join austenitic stainless steels. Neither preheating nor post-weld heat treatments are usually required.

Chemical Analysis

Weight % (all values are maximum unless a range is otherwise indicated)