Nicr15fe7tial Nickel Based Plate

Name: China Customized Nicr15fe7tial Nickel Based Plate Manufacturers Factory - Good Price - GNEE
Brand: GNEE
SKU: 218157072

Nickel-based alloy refers to a class of alloys with high strength and certain antioxidant corrosion resistance at 650 ~ 1000℃. According to the main properties, it is subdivided into nickel-based heat resistant alloy, nickel-based corrosion resistant alloy, nickel-based wear resistant alloy, nickel-based precision alloy and nickel-based shape memory alloy.

Have questions? GNEE sales representatives are available for live chat now

Send E-mail:info@gneestainless.com

Tel:+8615824687445

Send Inquiry Chat Now

Description

Gnee Steel (Tianjin) Co., Ltd. is one of the most professional manufacturers and suppliers of nicr15fe7tial nickel based plate in China. With abundant experience, we warmly welcome you to wholesale customized nicr15fe7tial nickel based plate from our factory. For price consultation, contact us.

NiCr15Fe7TiAl (Inconel X-750) nickel-based alloy sheet is engineered for extreme high-temperature environments, exhibiting exceptional creep resistance and rupture strength. The material maintains superior structural stability at temperatures up to 700°C, with a yield strength exceeding 600 MPa. Manufactured in strict accordance with the AMS 5542 standard, the alloy undergoes controlled solution annealing and precipitation hardening to ensure a uniform, dense distribution of precipitated phases, effectively resisting oxidation and intergranular corrosion. Prior to shipment, every sheet undergoes ultrasonic testing and precision tolerance checks to guarantee uniform thickness and the absence of internal defects, thereby ensuring outstanding physical reliability and long service life for critical components in aero-engines and gas turbines.

Nicr15fe7tial Nickel Based Plate

Inconel X-750 Plate

NiCr15Fe7TiAl (Inconel X-750) Specification

Parameter	Specification / Detail
Common Name	Inconel X-750
Material Standard	AMS 5542 / ASTM B670
Material Form	Plate / Sheet
Principal Characteristics	Excellent stress-rupture strength up to 700°C; High corrosion resistance
Processing State	Solution Treated + Precipitation Hardened
Melting Range	1300°C – 1430°C
Density	8.28 g/cm³

Chemical Composition (Weight %)

Element	Content (%)
Nickel (Ni)	70.0 min.
Chromium (Cr)	14.0 – 17.0
Iron (Fe)	5.0 – 9.0
Titanium (Ti)	2.25 – 2.75
Aluminum (Al)	0.40 – 1.00
Niobium (Nb+Ta)	0.70 – 1.20
Carbon (C)	≤ 0.08
Manganese (Mn)	≤ 1.00

Mechanical Properties (Room Temp)

Property	Value
Tensile Strength (UTS)	≥ 1000 MPa
Yield Strength (0.2% Offset)	≥ 600 MPa
Elongation	≥ 20%
Hardness	30 - 40 HRC (Heat treated)

Thermal Treatment & Processing Notes

Solution Treatment: Usually performed at 980°C – 1090°C followed by air cooling.

Aging (Precipitation Hardening):

Standard: 705°C for 20 hours followed by air cooling.

This process optimizes the formation of the (gamma prime) phase, providing maximum high-temperature strength.

Fabrication:

Welding: Good weldability; however, welding should be performed in the solution-treated condition.

Machinability: Due to high nickel and chromium content, it is considered a "difficult-to-machine" material. Use carbide-tipped tools with low speeds and high feed rates.

Nicr15fe7tial Nickel Based Plate Applications:

High-temperature springs and fasteners.

Gas turbine rotors and blades.

Nuclear power plant pressure vessels.

Heat-treating fixture components.

Price term	Ex-Work,FOB,CNF,CFR,CIF,etc
Export to	Kenya, Ireland, Singapore, Indonesia, Ukraine, Saudi Arabia, Spain, Canada, the United States, Brazil, Thailand, South Korea, India, Egypt, Oman, Malaysia, the Philippines, Kigali (Rwanda), etc.
Application	1)70% Ni was used for produce stainless steel and heat resistance steel 2)15% of the Ni in the world was used as electroplating. 3)Used as catalyst in oil industry