Stainless Steel DIN1 4306 1 4307 Flanges
Leave a message
DIN 1 4306 1 4307 SS Flanges are viral and reliable components used in the engineering and piping industries. DIN 1 4306 1 4307 stainless pipe flanges are made of austenitic stainless steel grade 304L or 304, respectively. They combine excellent corrosion-resistant properties with high temperatures, strength and hardness.
Stainless Steel DIN1.4306 1.4307 Pipe Flanges
Stainless Steel DIN1.4306 1.4307 Flanges are made from iron, chromium and nickel alloys. Chromium is the primary alloying element, giving the steel its corrosion resistance and characteristics, while nickel improves toughness and ductility. The mixture of these three chemical elements helps make this kind of stainless steel highly resistant to pitting, tarnishing and staining - perfect for any severe engineering structure or project. It is aesthetically pleasing with a glamorous sheen and durable enough to last generations.
DIN 1 4306 1 4307 SS Flanges are viral and reliable components used in the engineering and piping industries. DIN 1 4306 1 4307 stainless pipe flanges are made of austenitic stainless steel grade 304L or 304, respectively. They combine excellent corrosion-resistant properties with high temperatures, strength and hardness. Thanks to their superior quality, these durable flanges can be found in areas subject to heavy loads as well as in chemical and petrochemical applications. Furthermore, since they are prone to wear, SS DIN 1 4306 1 4307 Flanges need meagre maintenance costs and offer long-lasting service life even under harsh environmental conditions. As a result, they are an essential component of any industrial process that demands durability, reliability and superb performance at a great value.
1.4301/1.4307 X5CrNi18-10 / X2CrNi18-9, AISI 304/304L CHEMICAL COMPOSITION
| Grade | C | Si | Mn | P | S | Cr | Ni | Mo | Tio | Cu | Other |
|---|---|---|---|---|---|---|---|---|---|---|---|
| ACX 232 | <=0.030 | <=0.75 | <=2.00 | <=0.040 | <=0.030 | 18.00-20.00 | 10.00-11.00 | - | - | - | N(ppm) <700 |
Mechanical properties 1.4301/1.4307, X5CrNi18-10 / X2CrNi18-9, AISI 304/304L:
Tensile strength, Rm 460 - 700 N/mm2
Yield strength, Rp0,2: >190 N/mm2
Elongation, A: >45%
Impact strength, KV: >60J
Modulus of elasticity, E: 200 GPa
Hardness, HB: <215
Linear expansion coefficient, α: 16,0 * 10-6 K-1
Thermal capacity, cp20℃: 500 J * kg-1 * K-1
Thermal conductivity, λ: 15 W * m-1 * K-1
Resitivity, Ω: 0,73 mkOhm*m